AWS 型號 |
產品牌號 |
焊絲化學成份 |
特性簡單介紹 |
|
|
C |
Mn |
Si |
S |
P |
|
|
ER70S-3 |
NERTALIC 70S |
0.08 |
1.15 |
0.6 |
0.015 |
0.015 |
|
|
ER70S-6 |
NERTALIC 70A |
0.08 |
1.4 |
0.8 |
0.015 |
0.015 |
|
|
ER80SG |
CARBOFIL Cr Mo 1 |
0.08 |
1.4 |
0.8 |
|
Mo:0.6
Cr:1.1 |
焊接σ s ≥ 420Mpa 高強鋼 |
ER110S-G |
NERTALIC 88 |
0.05 |
1.9 |
0.45 |
0.010 |
0.010 |
Ni:2.0
Mo:0.55 |
焊接σ s ≥ 650Mpa 高強鋼，用于 ELDOX 700 鋼， WEDOX900 低強匹配焊 |
ER100S-G |
CARBOFIL Ni Mo Cr |
≤ 0.01 |
1.6 |
0.6 |
|
Ni:1.4,Mo:0.25,Cr:0.3 |
焊接σ s ≥ 690Mpa 高強鋼，用于 WELDOX 700 鋼， WEDOX900 低強匹配焊 |
ER90S-G |
CARBOFIL Ni Mo 1 |
≤ 0.10 |
1.8 |
0.6 |
|
|
Ni:1.0
Mo:0.4
Ti:0.15 |
焊接σ s ≥ 620Mpa 高強鋼 |
ER120S-G |
ED-FK 1000 |
0.10 |
1.80 |
0.80 |
|
Mo:0.50,Ni:2.20 |
焊接σ s ≥ 620Mpa 高強鋼，用于 WELDOX900 ， 960 鋼 |
ER90S-B3 |
OE CrMo2 |
0.08 |
1.1 |
0.6 |
|
|
Cr:2.7
Mo:1.0 |
焊接 2.25%Cr-1%Mo 耐熱鋼 |
ER90S-B9 |
OE-CrMo91V |
0.10 |
0.50 |
Si:0.4,Cr:11.5,Mo:1.0,W:0.5,V:0.3 |
|
9Cr1MoV(P91,T91) 耐熱鋼焊接 |
|
|